D232/M3 – Orchard Management

Main Features

Low gloss, extrusion

Density: 1.04

Main Applications

Extrusion/coextrusion of sheets
with matt surfac

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	8
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	27
Strain at break	50 mm/min	ASTM D 638	%	100
Flexural Strength	2 mm/min	ASTM D 790	MPa	40
Flexural Modulus	2 mm/min	ASTM D 790	MPa	1550
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	110
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	90
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	80
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	75
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	9.5
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	79
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	R97
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R103
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	106
	50 N – 120°C/h	ISO 306/B120	ºC	101
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	101
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³