ABS-Rubber – Page 2 – Orchard Management

Main Features

Bitumen modification in waterproofing systems, formulated compounds for shoe soles and technical goods

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Methods	Analytical Manual	Units
General
Mooney Viscosity	ASTM D1646	MPP16	ML1+4 @ 100°C	N/A
Bound Styrene	ASTM D5775	MPP5-MPP6	wt %	34 – 38
Block styrene	ASTM D3314	MPP8	wt %	100
Solution viscosity*	ASTM D5774	MPP9	cPs	N/A
Gel content		MPP12	arbitrary	N/A
Molecular weight		MPP1	KDalton	245 – 275
Coupling efficiency		MPP1	%	85 min
Volatile matter content	ASTM D5668	MPP10	wt %	1 max
Residual solvent		MPP18	ppm	< 10
Colour	ASTM E313	MPP13	Yellow index	15 max
Solution color (Pt/Co)	ASTM D1209		arbitrary	N/A
Vinyl content		MPP5-MPP6	wt % on butadiene	10.0 – 14.0
Ash content	ASTM D5667	MPP15	wt %	N/A
Solvent extractables	ASTM D5774	MPP11	wt %	N/A

ABS-Rubber

Main Feautures

Mainly used in plastic material (PS, ABS)modification.

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Methods	Analytical Manual	Units
General
Mooney Viscosity	ASTM D1646	MPP16	ML1+4 @ 100°C	60 – 80
Bound Styrene	ASTM D5775	MPP5-MPP6	wt %	9.0 – 11.0
Block styrene	ASTM D3314	MPP8	wt %	4 – 6
Solution viscosity*	ASTM D5774	MPP9	cPs	N/A
Gel content		MPP12	arbitrary	N/A
Molecular weight		MPP1	KDalton	N/A
Coupling efficiency		MPP1	%	N/A
Volatile matter content	ASTM D5668	MPP10	wt %	0.75 max
Residual solvent		MPP18	ppm	N/A
Colour	ASTM E313	MPP13	Yellow index	N/A
Solution color (Pt/Co)	ASTM D1209		arbitrary	N/A
Vinyl content		MPP5-MPP6	wt % on butadiene	9.0 – 11.0
Ash content	ASTM D5667	MPP15	wt %	0.2 max
Solvent extractables	ASTM D5774	MPP11	wt %	N/A

ABS-Rubber

Main Features

The star like structure of P30 guarantees value in viscosity and, contemporary, a molecular weight sufficiently high.
The high capacity of loading carbon black and good extrudibility made this grade suita abrasion strips
Construction in tire building.

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Methods	Analytical Manual	Units
General
Mooney Viscosity	ASTM D1646	MPP16	ML1+4 @ 100°C	45 – 55
Bound Styrene	ASTM D5775	MPP5-MPP6	wt %	N/A
Block styrene	ASTM D3314	MPP8	wt %	N/A
Solution viscosity*	ASTM D5774	MPP9	cPs	35 – 50
Gel content		MPP12	arbitrary	4 max
Molecular weight		MPP1	KDalton	N/A
Coupling efficiency		MPP1	%	N/A
Volatile matter content	ASTM D5668	MPP10	wt %	0.75 max
Residual solvent		MPP18	ppm	N/A
Colour	ASTM E313	MPP13	Yellow index	N/A
Solution color (Pt/Co)	ASTM D1209		arbitrary	10 max
Vinyl content		MPP5-MPP6	wt % on butadiene	11 – 13
Ash content	ASTM D5667	MPP15	wt %	0.2 max
Solvent extractables	ASTM D5774	MPP11	wt %	N/A

ABS-Rubber

BR245

Main Features

BR245 rubber is a solution polymerized low cis star
Branched, low coupled, dry
Polybutadiene produced using alkyl lithium initiator in batch reactors.

Main Applications

BR 245 polybutadiene is used in tire compounds and in some mechanical good compounds. Good hysteresis properties of BR 245 allow it to be blended with natural rubber to produce enhanced properties in truck tire treads. The addition of polybutadiene low cis to natural rubber upgrades abrasion and cracking resistance, maintains good resilience and also provides better resistance to overcure and degradation during aging. BR 245 and SOL R 1204 were tried in blends with natural rubber in large size passengers tyre reducing groove cracking compared to natural rubber.

Keys

BR245 rubber is a solution polymerized low cis star branched, low coupled, dry polybutadiene produced using alkyl lithium initiator in batch reactors.

Properties	Test Methods	Analytical Manual	Units
General
Mooney Viscosity	ASTM D1646	MPP16	ML1+4 @ 100°C	50 – 60
Bound Styrene	ASTM D5775	MPP5-MPP6	wt %	N/A
Block styrene	ASTM D3314	MPP8	wt %	N/A
Solution viscosity*	ASTM D5774	MPP9	cPs	N/A
Gel content		MPP12	arbitrary	N/A
Molecular weight		MPP1	KDalton	N/A
Coupling efficiency		MPP1	%	N/A
Volatile matter content	ASTM D5668	MPP10	wt %	0.6 max
Residual solvent		MPP18	ppm	N/A
Colour	ASTM E313	MPP13	Yellow index	N/A
Solution color (Pt/Co)	ASTM D1209		arbitrary	N/A
Vinyl content		MPP5-MPP6	wt % on butadiene	11 – 13
Ash content	ASTM D5667	MPP15	wt %	0.08
Solvent extractables	ASTM D5774	MPP11	wt %	N/A

ABS-Rubber

BR 277

Main Features

BR277 rubber is a solution polymerized low cis star branched, low efficiency coupled, oil extended polybutadiene produced using alkyl lithium initiator in batch reactors.

Keys

BR 277 oil extended polybutadiene is used in tire compounds and in some mechanical good compounds.

Properties	Test Methods	Analytical Manual	Units
General
Mooney Viscosity	ASTM D1646	MPP16	ML1+4 @ 100°C	37 – 47
Bound Styrene	ASTM D5775	MPP5-MPP6	wt %	N/A
Block styrene	ASTM D3314	MPP8	wt %	N/A
Solution viscosity*	ASTM D5774	MPP9	cPs	N/A
Gel content		MPP12	arbitrary	N/A
Molecular weight		MPP1	KDalton	N/A
Coupling efficiency		MPP1	%	N/A
Volatile matter content	ASTM D5668	MPP10	wt %	0.3 max
Residual solvent		MPP18	ppm	N/A
Colour	ASTM E313	MPP13	Yellow index	N/A
Solution color (Pt/Co)	ASTM D1209		arbitrary	N/A
Vinyl content		MPP5-MPP6	wt % on butadiene	11 – 13
Ash content	ASTM D5667	MPP15	wt %	0.04
Solvent extractables	ASTM D5774	MPP11	wt %	26.3–29.3

ABS-Rubber

B532/E

B432/E
Main Feautures

Sheets and profile.
Good impact strength
High toughness

Density: 1.04
Main Application

Plain or coextruded with high draw
Ratios for refrigeration, sanitary
Automotive,
Packaging, housholding (profiles)

Density: 1.04
Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	5
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	35
Strain at break	50 mm/min	ASTM D 638	%	45
Flexural Strength	2 mm/min	ASTM D 790	MPa	68
Flexural Modulus	2 mm/min	ASTM D 790	MPa	2300
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	280
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	190
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	150
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	125
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	20
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	10
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	16
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R110
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	108
	50 N – 120°C/h	ISO 306/B120	ºC	104
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	104
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6

Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

About

Category: ABS-Rubber

SOL T6306

Main Features

SOL B183

Main Feautures

Keys

Intene P30

Main Features

Keys

BR245

Main Features

Main Applications

Keys

BR 277

Main Features

Keys

B532/E

B432/E
Main Feautures

Density: 1.04
Main Application

Density: 1.04
Keys

Category: ABS-Rubber

Main Features

Main Feautures

Keys

Main Features

Keys

Main Features

Main Applications

Keys

Main Features

Keys

B432/E Main Feautures

Density: 1.04 Main Application

Density: 1.04 Keys

B432/E
Main Feautures

Density: 1.04
Main Application

Density: 1.04
Keys