ABS-Rubber – Orchard Management

F332

siteadmin — Mon, 04 Dec 2023 14:37:12 +0000

Main Features

General purpose
Self-coloring

Density: 1.04

Main Applications

Households
Small Appliances
and white goods Vacuum Cleaners
Electrical components for civil and industrial applications

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	14
Mechanical
Tensile Strength	50mm/min	ASTM D 638	MPa	42
Strain at break	50mm/min	ASTM D 638	%	60
Flexural Strength	2mm/min	ASTM D 790	MPa	60
Flexural Modulus	2mm/min	ASTM D 790	MPa	2250
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	190
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	125
	-20°C – thickness 3.2 mm	ISO 180/4A	J/m	100
	-40°C – thickness 3.2 mm	ISO 180/4A	J/m	90
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	14
	-40°C – thickness 4 mm	ISO 180/1A	kJ/m²	8
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	13
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	-40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R110
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	°C	107
	50 N – 120°C/h	ISO 306/B120	°C	102
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	°C	101
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	°C	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

E332

siteadmin — Mon, 04 Dec 2023 14:33:33 +0000

Main Features

Medium heat
Resistance, goo flow, good impact strength

Density: 1.04

Main Applications

Automative Interior (Trim parts)
Tiles

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	10
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	40
Strain at break	50 mm/min	ASTM D 638	%	75
Flexural Strength	2 mm/min	ASTM D 790	MPa	62
Flexural Modulus	2 mm/min	ASTM D 790	MPa	2200
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	190
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	115
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	90
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	85
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	15
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	8
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	12
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R111
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	109
	50 N – 120°C/h	ISO 306/B120	ºC	104
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	103
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

L322

siteadmin — Mon, 04 Dec 2023 14:29:45 +0000

Main Features

Medium heat injection
Moulding, high flow
Good thermal
Stability during processing

Density: 1.04

Main Application

Domestic appliances
Thermal resistant items(front panels, frames etc.)
Electrical sector

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	23
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	45
Strain at break	50 mm/min	ASTM D 638	%	20
Flexural Strength	2 mm/min	ASTM D 790	MPa	69
Flexural Modulus	2 mm/min	ASTM D 790	MPa	2350
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	170
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	100
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	70
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	50
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	13
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	6
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	10
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R109
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	99
	50 N – 120°C/h	ISO 306/B120	ºC	96
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	96
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

F232

siteadmin — Mon, 04 Dec 2023 14:26:48 +0000

Main Features

General purpose,
High flow injection moulding
Grade, good impact

Density: 1.04

Main Applications

Small and large
Household appliances
Vacuum cleaners
Toys
Telephones and consumer electronics

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	14
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	45
Strain at break	50 mm/min	ASTM D 638	%	20
Flexural Strength	2 mm/min	ASTM D 790	MPa	69
Flexural Modulus	2 mm/min	ASTM D 790	MPa	2350
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	170
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	100
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	70
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	50
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	13
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	6
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	10
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R109
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	107
	50 N – 120°C/h	ISO 306/B120	ºC	101
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	102
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

B432/E

siteadmin — Mon, 04 Dec 2023 14:23:11 +0000

Main Features

Sheets and profile Medium
Impact strength

Density: 1.04

Main Applications

Plain or coextruded with high draw
Ratios for refrigeration, sanitary
Automotive, packaging,
Housholding (profiles)

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	5
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	35
Strain at break	50 mm/min	ASTM D 638	%	45
Flexural Strength	2 mm/min	ASTM D 790	MPa	68
Flexural Modulus	2 mm/min	ASTM D 790	MPa	2300
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	280
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	190
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	150
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	125
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	20
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	10
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	16
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R110
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	108
	50 N – 120°C/h	ISO 306/B120	ºC	104
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	104
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6

Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

B732/E

siteadmin — Mon, 04 Dec 2023 14:20:16 +0000

Main Features

Very high
Impact strength

Density: 1.04

Main Applications

Extrusion of thick sheets for sanitary
Automotive applications

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	4.5
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	45
Strain at break	50 mm/min	ASTM D 638	%	45
Flexural Strength	2 mm/min	ASTM D 790	MPa	60
Flexural Modulus	2 mm/min	ASTM D 790	MPa	2200
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	350
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	300
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	200
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	140
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	28
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	12
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	20
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R103
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	109
	50 N – 120°C/h	ISO 306/B120	ºC	104
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	100
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

D232/M3

siteadmin — Mon, 04 Dec 2023 14:16:51 +0000

Main Features

Low gloss, extrusion

Density: 1.04

Main Applications

Extrusion/coextrusion of sheets
with matt surfac

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	8
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	27
Strain at break	50 mm/min	ASTM D 638	%	100
Flexural Strength	2 mm/min	ASTM D 790	MPa	40
Flexural Modulus	2 mm/min	ASTM D 790	MPa	1550
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	110
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	90
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	80
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	75
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	9.5
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	79
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	R97
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R103
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	106
	50 N – 120°C/h	ISO 306/B120	ºC	101
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	101
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

C442

siteadmin — Mon, 04 Dec 2023 14:13:26 +0000

Main Features

Heat resistance
Good flow
Good impact strength

Density: 1.04

Main Applications

Automotive interior (extruded profiles, interior trim),

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Condition	Test Methods	Units
General
Density		ISO 1183	g/cm3	1.04
Water Absorption		ASTM D 570	%	0.3
Rheological
Melt Flow Rate (MFR)		ISO 1133	g/10min	6
Mechanical
Tensile Strength	50 mm/min	ASTM D 638	MPa	43
Strain at break	50 mm/min	ASTM D 638	%	45
Flexural Strength	2 mm/min	ASTM D 790	MPa	65
Flexural Modulus	2 mm/min	ASTM D 790	MPa	2300
Izod Impact Strength Notched	+23°C – thickness 3.2 mm	ISO 180/4A	J/m	200
	0°C – thickness 3.2 mm	ISO 180/4A	J/m	165
	– 20°C – thickness 3.2 mm	ISO 180/4A	J/m	125
	– 40°C – thickness 3.2 mm	ISO 180/4A	J/m	100
	+23°C – thickness 4 mm	ISO 180/1A	kJ/m²	17
	– 40°C – thickness 4 mm	ISO 180/1A	kJ/m²	9
Charpy Impact Strength, Notched	+23°C	DIN 53453	kJ/m²	12
Unnotched	+23°C	DIN 53453	kJ/m²	NB
Unnotched	– 40°C	DIN 53453	kJ/m²	NB
Rockwell Hardness	scale R	ISO 2039/2	kJ/m²	R110
Thermal
Vicat Softening Tempreture	10 N – 120°C/h	ISO 306/A120	ºC	114
	50 N – 120°C/h	ISO 306/B120	ºC	108
Deflection temp. under load (annealed)	1.8 MPa – 120°C/h	ASTM D 648	ºC	108
Ceofficient of linear thermal expansion		ASTM D 696	10 -5/ºC	9
Thermal Conductivity		ASTM C 177	W/(Km)	0.17
Moulding Shrinkage		ISO 294.4	%	0.4-0.6
Flammability
Flame behavior	thickness 1.5 mm	UL 94	class	HB
Glow wire test	thickness 3 mm	IEC 60695-2-1	ºC	650
Electrical
Surface resistivity	dry	IEC 60093	ohm	10+14
Volume resistivity	dry	IEC 60093	ohm*cm	10+15
Dielectric strength	dry	IEC 60243	kV/mm	30
Dielectric constant (relative permittivity)	1000 Hz – dry	IEC 60250		3.1
Dissipation factor	1000 Hz – dry	IEC 60250		15*10-³

SOL T6302

siteadmin — Mon, 04 Dec 2023 14:09:43 +0000

Main Features

Bitumen modification,
Automotive interior
Extruded profiles, interior trim

Density: 1.04

Main Applications

Automotive interior (extruded profiles, interior trim),

Density: 1.04

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Methods	Analytical Manual	Units
General
Mooney Viscosity	ASTM D1646	MPP16	ML1+4 @ 100°C	N/A
Bound Styrene	ASTM D5775	MPP5-MPP6	wt %	29 – 33
Block styrene	ASTM D3314	MPP8	wt %	100
Solution viscosity*	ASTM D5774	MPP9	cPs	N/A
Gel content		MPP12	arbitrary	N/A
Molecular weight		MPP1	KDalton	95 – 125
Coupling efficiency		MPP1	%	84 min
Volatile matter content	ASTM D5668	MPP10	wt %	1 max
Residual solvent		MPP18	ppm	< 10
Colour	ASTM E313	MPP13	Yellow index	10 max
Solution color (Pt/Co)	ASTM D1209		arbitrary	N/A
Vinyl content		MPP5-MPP6	wt % on butadiene	10.0 – 14.0
Ash content	ASTM D5667	MPP15	wt %	N/A
Solvent extractables	ASTM D5774	MPP11	wt %	N/A

SOL T161B

siteadmin — Mon, 04 Dec 2023 14:04:48 +0000

Main Features

Bitumen modification for waterproofing membranes used in roofing and bridge insulation, road paving & pipe coating

Keys

Packaged product should be protected from the atmosferic agents and stored out of direct sunlight
NB: No Break
/M: Matt – Digit following letter
/M indicates increasing values of mattness

Properties	Test Methods	Analytical Manual	Units
General
Mooney Viscosity	ASTM D1646	MPP16	ML1+4 @ 100°C	N/A
Bound Styrene	ASTM D5775	MPP5-MPP6	wt %	29 – 33
Block styrene	ASTM D3314	MPP8	wt %	100
Solution viscosity*	ASTM D5774	MPP9	cPs	N/A
Gel content		MPP12	arbitrary	N/A
Molecular weight		MPP1	KDalton	220 – 260
Coupling efficiency		MPP1	%	84 min
Volatile matter content	ASTM D5668	MPP10	wt %	1 max
Residual solvent		MPP18	ppm	< 10
Colour	ASTM E313	MPP13	Yellow index	10 max
Solution color (Pt/Co)	ASTM D1209		arbitrary	N/A
Vinyl content		MPP5-MPP6	wt % on butadiene	10.0 – 14.0
Ash content	ASTM D5667	MPP15	wt %	N/A
Solvent extractables	ASTM D5774	MPP11	wt %	N/A